Fabrication and characterization of YBCO (358) system
Is this your thesis?
This record came from a bulk archive import. If it’s yours, link it to your profile.
Abstract (EN)
In this thesis Y3Ba5Cu8Ox samples, which are the member of Y-358 superconducting system, have been prepared by using solid - state reaction method. After calcinations stage samples were heat treated at between 850 0C - 920 0C 24 hours. After than microstructural, electrical and magnetic properties of samples prepared were investigated and superconductivity behavior was characterized.As a result of this work it was obtained that, samples prepared with a large temperature band showed a superconductivity behavior. All samples prepared showed a similar characteristics of Y-123 superconducting compound. No sign of superconductivity over 100 K were obtained.
Author
Filiz Kurt
How to Cite
Filiz Kurt (Master Thesis). Fabrication and characterization of YBCO (358) system, 2011, İnönü University.
Keywords
License
Tüm Hakları Saklıdır
This work is shared under the specified license terms.
More theses from İnönü University
- Researching the effect of avenanthramide C on breast cancer(2022)
- Regional threats and opportunities to turkey's national economic security(2022)
- Atatürk'ün çağdaşlaşma anlayışı(2009)
- Knowledge and logic in Hans Reichenbach(2026)
- Language scientific features of the Arab dialectal spoken in the harran region and oral literature materials(2022)
- The Battle of Nablus place and importance in war history(2023)