Effects of technological properties on scoth pine (Pinus sylvestris L.) of some mordant and varnishes

Various technological properties have been determined by applying impregnation treatment to yellowing wood at various vacuum / diffusion times and applying water based varnish. The impregnation process has been complied with ASTM 1413 76; care has been taken to ensure that the impregnate materials used are particularly environmentally friendly (environment / human etc.). The highest% retention was found in aluminum sulphate (9.90%) and lowest boric acid (1.07%). The maximum air mass after impregnation was determined in Aluminum sulphate (0.56 g / cm3) for 40 minutes vacuum / 40 minutes diffusion duration. the highest modulus of elasticity was determined in the water-based varnish (8900N / mm2), the highest pressure resistance Boric acid (68.53 N / mm2), the highest bending strength in water-based varnish (105.36 N / mm2) Usage levels are available in the furniture and construction industry (indoor / outdoor).