ZnO nanoyapıların üretilmesi, karakterizasyonu ve uygulama alanlarının araştırılması

It is common knowledge that zinc oxide (ZnO) as a substantial semiconductor material because of its broad band gap (3.37eV) and good seperation energy (60 meV). Anodic oxidation of ZnO molecules have drawn interest because of their cost-effective synthesis, high efficiency and simplicity of the process. Anodization parameters (voltage, time, ph, electrolyte) can influence the morphology of ZnO. Also, ZnO is widely used in several implementations such as photovoltaic cell, chemical sensor, antibacterial agent and photocatalysts. Structures and different morphologies of ZnO can exert influence on its photocatalytic activity. In this thesis, ZnO nanostructures were produced succesfully through anodic oxidation method. Before anodization, a large portion of bulk Zn was cut off into nine pieces with dimensions 3x3 cm2. These samples were sanded up to acquire the appropriate material surface. After that, samples sonicated in ethanol, acetone and deionized water in an ultrasonic bath for ten minutes separately. Produced ZnO samples were heat treated at 300 °C for one hour with the heating rate of 5 °C/minute. The synthesized ZnO nanostructures were characterized to investigate their structure, elemental composition, photocatalytic activity and morphology with aid of X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy and UV-Vis spectrophotometer. Concludes from this produced ZnO specimens can make use of as photocatalyst.