Preparation and characterization of polypropylene (PP) based nanocomposites containing some boron compounds

In this thesis study, PP and TPU polymers are used as matrix material. Nano-particle boron compounds (h-BN, B2O3) containing PP, TPU composite material. These composite materials were analyzed by structural (FT-IR), thermal (DSC and TGA), mechanical (Stretch-Tension, DMA, Three point bending) and Shore-D hardness points and morphological (SEM) analyzes. For BCK-5 composite samples containing 2% h-BN with MKC-4 composite and 2% B2O3, the BCK-5 sample shows that the degradation grade starts at lower temperature values. In addition, when the h-BN and B2O3 reinforcement materials were compared, it is seen that the distribution of B2O3 particles with in the structure was heterogeneous and compared to with h-BN supplement containing MKC-4 composite with and supplementation.