Coating of bioceramics consisting of different silica sources on ti6al4v metal substrate using hvof technique
2018
0 görüntülenme
0 i̇ndirme
Danışman: Doç. Dr. Atilla Evcin
Özet (EN)
In this study, different SiO2 added bioceramics were coated on Ti6AI4V metal substrate. Widely used implant material Ti6AI4V was coated with SiO2 added hydroxyapatite and coating was characterized. Mineralogical anaylsis of coating material, coating thickness, contact angle and weight gain after holding SBF datas were measured and corrosion analysis were carried out. As a result of the analysis, it's observed that diatomite-added, SiO2-added and bioactive glass-added hydroxyapatite powders gave more superior results to coatings made with pure hydroxyapatite powder.
Yazar
Dr. Betül Gökçen Bohur
Kurum
Afyon Kocatepe University
Malzeme Bilimi ve Mühendisliği Bilim Dalı
Bu Yayına Nasıl Atıf Yapılır
Betül Gökçen Bohur (Master Thesis). Coating of bioceramics consisting of different silica sources on ti6al4v metal substrate using hvof technique, 2018, Afyon Kocatepe University.
Anahtar Kelimeler
Lisans
Tüm Hakları Saklıdır
Bu eser belirtilen lisans koşulları altında paylaşılmaktadır.
Afyon Kocatepe University tezlerinden daha fazlası
- SURFACE ACCURACY MEASUREMENTS OF A FOLDABLE COMPOSITE REFLECTOR(2012)
- Comparative proteomics analyses of flowers at different development stages in Thermopsis turcica, endemic to Turkey(2016)
- The effect of employees' trust in supervisors and their quality of working life on their intention to leave job: A study in five star thermal hotels in Afyonkarahisar(2016)
- On the Pasch geometry(2017)
- On the characterization of circle-preserving maps(2017)
- Investigation of possible genotoxic effects of oxadiazone and pendimethaline herbicides by comet and micronucleus test systems(2017)